Cloverleaf microgyroscope with through-wafer interconnects and method of manufacturing a cloverleaf microgyroscope with through-wafer interconnects

ABSTRACT

The present invention relates to a method of manufacturing a cloverleaf microgyroscope containing an integrated post comprising: attaching a post wafer to a resonator wafer, forming a bottom post from the post wafer being attached to the resonator wafer, preparing a base wafer with through-wafer interconnects, attaching the resonator wafer to the base wafer, wherein the bottom post fits into a post hole in the base wafer, forming a top post from the resonator wafer, wherein the bottom and top post are formed symmetrically around the same axis, and attaching a cap wafer on top of the base wafer.

BACKROUND OF THE INVENTION

1. Field of the Invention

The present invention refers to a cloverleaf microgyroscope and a method of manufacturing a cloverleaf microgyroscope that contains a single crystal silicon cloverleaf-shaped resonator and integrated post attached to the leaves with through-wafer interconnects.

2. Description of Related Art

U.S. Pat. No. 5,894,090 to Tang et al., which is incorporated herein by reference, discloses a micromachined symmetrical leaf structure having a plurality of symmetrically disposed leaves about a defined center. At least one micromachined spring is disposed symmetrically with respect to the symmetrical leaf structure and supporting the symmetrical leaf structure, a rim/base structure to which the spring is coupled. The rim/base structure includes a plurality of sensing and drive electrodes and a circuit electrically coupled to the electrodes included within the rim/base structure. The circuit provides drive signals to the drive electrodes to oscillate the symmetrical leaf structure and to receive a sensing signal from the sensing electrodes to detect response of the oscillating symmetrical leaf structure to physical phenomena exterior to the micromachined resonator. The micromachined resonator has a manually inserted post. It shows a lack of a silicon based vacuum encapsulation. A low yield is obtained during the separation. The manufacturing of the resonator involves high fabrication costs. It shows large vibration sensitivity and no clear path to electronic integration.

The known manufacturing processes make it very difficult to manufacture a microgyroscope. The central post is inserted by hand, the device has to be vacuum packaged in a custom package and there is no ability to integrate control electronics with the silicon structure.

Although electrical through-wafer vias have been used for many years for standard ICs, the use of deep (>500 microns) vias with MEMS within a wafer-level vacuum package has not been attempted to our knowledge. In addition, standard pn junction techniques for electrical isolation are not satisfactory for the extremely high levels of isolation that must be achieved for MEMS devices. Also, standard poly fills of etched vias are not useful since the front side contacts (control electrodes for the MEMS device) must be perfectly smooth for the microgyro. This is needed to produce a high degree of reproducibility of the measured capacitance between the plates. The use of spray resist techniques allows us to perform lithography in high-aspect ratio holes, and thus create the desired structure.

What are needed are a cloverleaf microgyroscope and a process for manufacturing a cloverleaf microgyroscope with an integrated central post and electronics with the resonator and vacuum package at wafer-level with a single crystal silicon construction.

BRIEF SUMMARY OF THE INVENTION

This invention addresses the above needs.

One aspect of the present invention is a method of manufacturing a cloverleaf microgyroscope containing an integrated post comprising:

-   -   a) attaching a post wafer to a resonator wafer,     -   b) forming a bottom post from the post wafer,     -   c) preparing a base wafer with through-wafer interconnects,     -   d) attaching the resonator wafer to the base wafer, wherein the         bottom post fits into a post hole in the base wafer,     -   e) forming a top post from the resonator wafer, wherein the         bottom and top post are formed symmetrically around the same         axis, and     -   f) attaching a cap wafer on top of the base wafer.

Another aspect of the present invention is a cloverleaf microgyroscope manufactured by this method.

The construction of a microgyroscope has a single crystal silicon cloverleaf-shaped resonator and integrated post attached to the leaves. The microgyroscope device array is fabricated by bonding two separate substrates together using a gold/gold thermo compression technique; one contains the cloverleaf resonator structures fabricated from silicon-on-insulator (SOI) and bulk silicon substrates, and the other contains the support pillars and electrode metal. A fourth wafer containing an array of etched cavities and openings which allow the bonding of electrical wires from metal pads to the device wafer in a vacuum, thus hermetically sealing each individual microgyroscope.

This disclosure describes a new concept of using deep through-wafer vias combined with wafer-level vacuum packaging to produce all-Si microgyros with ball-grid array interconnects on the bottom wafer. High-aspect ratio lithography using spray-on resist and DRIE are utilized with conformal dielectric coatings and metal plating from the backside to form the through-wafer interconnects. For base wafer thicknesses of about 800 microns, the proposed lateral dimension of the vias is about 200 microns, which is consistent with the size of the gyro's control electrodes.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

These and other features, aspects and advantages of the present invention will become better understood with reference to the following description, appended claims, and accompanying drawings where

FIG. 1 a is a top plan view of the preferred starting material of a resonator SOI wafer A and FIG. 1 b is a cross-sectional view through wafer A of FIG. 1 a at line 1 b—1 b of the resonator SOI wafer A;

FIG. 2 a is a top plan view of the preferred starting material of a resonator SOI wafer A and FIG. 2 b is a cross-sectional view through wafer A of FIG. 2 a at line 2 b—2 b of the resonator SOI wafer A;

FIG. 3 a is a top plan view of the preferred starting material of a resonator SOI wafer B and FIG. 3 b is a cross-sectional view through wafer B of FIG. 3 a at line 3 b—3 b of the bottom-portion wafer B;

FIG. 4 a is a cross-sectional view at line 3 b—3 b of the bond wafer B;

FIG. 4 b is a cross-sectional view at line 2 b—2 b of bonded to wafer A;

FIG. 5 a is a top plan view of the resonator SOI wafer A and a bottom post B′ and FIG. 5 b is a cross-sectional view through wafer A and bottom post B′ of FIG. 5 a at line 5 b—5 b of the resonator SOI wafer A and bottom post B′;

FIG. 6 a is a top plan view of the resonator SOI wafer A and a bottom post B′ and FIG. 6 b is a cross-sectional view through wafer A and bottom post B′ of FIG. 6 a at line 6 b—6 b of the resonator SOI wafer A and bottom post B′ after several contacts are attached to it;

FIG. 7 a is a top plan view of the preferred starting material of a base wafer C and FIG. 7 b is a cross-sectional view through wafer C of FIG. 7 a at line 7 b—7 b of the base wafer C;

FIG. 8 a is a top plan view of the preferred starting material of the base wafer C and FIG. 8 b is a cross-sectional view through wafer C of FIG. 8 a at line 8 b—8 b of the base wafer C, after on both surfaces of base wafer C a silicon dioxide layer is grown;

FIG. 9 a is a top plan view of the preferred starting material of the base wafer C and FIG. 9 b is a cross-sectional view through wafer C of FIG. 9 a at line 9 b—9 b of the base wafer C, after pillar fabrication;

FIG 10 a is a top plan view of the preferred starting material of the base wafer C and FIG. 10 b is a cross-sectional view through wafer C of FIG. 10 a at line 10 b—10 b of the base wafer C, after on both surfaces of base wafer C a silicon dioxide layer is grown;

FIG. 11 a is a top plan view of the preferred starting material of the base wafer C and FIG. 11 b is a cross-sectional view through wafer C of FIG. 11 a at line 11 b—11 b of the base wafer C after an ohmic contact.

FIG. 12 a is a top plan view of the preferred starting material of the base wafer C and FIG. 12 b is a cross-sectional view through wafer C of FIG. 12 a at line 12 b—12 b of the base wafer C after front side metal deposition.

FIG. 13 a is a bottom view of the preferred starting material of the base wafer C and FIG. 13 b is a cross-sectional view through wafer C of FIG. 13 a at line 13 b—13 b of the base wafer C after hole formation on the bottom of base wafer C;

FIG. 14 a is a bottom view of the preferred starting material of the base wafer C and FIG. 14 b is a cross-sectional view through wafer C of FIG. 14 a at line 14 b—14 b of the base wafer C after dielectric layer deposition on the bottom of base wafer C;

FIG. 15 a is a bottom view of the preferred starting material of the base wafer C and FIG. 15 b is a cross-sectional view through wafer C of FIG. 15 a at line 15 b—15 b of the base wafer C after Ti metal etch on the bottom of base wafer C;

FIG. 16 a is a bottom view of the preferred starting material of the base wafer C and FIG. 16 b is a cross-sectional view through wafer C of FIG. 16 a at line 16 b—16 b of the base wafer C after hole metal plating on the bottom of base wafer C;

FIG. 17 a is a bottom view of the preferred starting material of the base wafer C and FIG. 17 b is a cross-sectional view through wafer C of FIG. 17 a at line 17 b—17 b of the base wafer C after dielectric layer removal on the bottom of base wafer C;

FIG. 18 a is a top plan view of the preferred starting material of the base wafer C and FIG. 18 b is a cross-sectional view through wafer C of FIG. 18 a at line 18 b—18 b of the base wafer C after front-side electrode and seal ring metal patterning and deposition on the base wafer C;

FIG. 19 a is a top plan view of the preferred starting material of the base wafer C and FIG. 19 b is a cross-sectional view through wafer C of FIG. 19 a at line 19 b—19 b of the base wafer C after a post hole etch is carried out in the base wafer C;

FIG. 20 a is a top plan view of the preferred starting material of the bottom surface of wafer A and FIG. 20 b is a cross-sectional view through the base wafer A, post B′, and base wafer C of FIG. 20 a at line 20 b—20 b of the base wafer A, post B′, and base wafer C;

FIG. 21 a is a top plan view depicting post A′ and base wafer C and FIG. 21 b is a cross-sectional view through the base wafer A, post B′, and base wafer C of FIG. 21 a at line 21 b—21 b depicting post A′, post B′, and base wafer C after post formation;

FIG. 22 a is a bottom view of the preferred starting material of a cap wafer D and FIG. 22 b is a cross-sectional view through the cap wafer D of FIG. 22 a at line 22 b—22 b of the cap wafer D;

FIG. 23 a is a bottom view of the preferred starting material of a cap wafer D and FIG. 23 b is a cross-sectional view through the cap wafer D of FIG. 23 a at line 23 b—23 b of the cap wafer D after backside metallization;

FIG. 24 a is a bottom view of the preferred starting material of a cap wafer D and FIG. 24 b is a cross-sectional view through the cap wafer D of FIG. 24 a at line 24 b—24 b of the cap wafer D after forming of backside cavity;

FIG. 25 a is a top plan view of the preferred starting material of a cap wafer D and FIG. 25 b is a cross-sectional view through the cap wafer D and the base wafer C of FIG. 25 a at line 25 b—25 b of the cap wafer D bonded to the base wafer C.

DETAILED DESCRIPTION

The following disclosure provides the construction of a microgyroscope that has a single crystal silicon cloverleaf-shaped resonator and integrated post attached to the leaves. The microgyroscope device is fabricated by bonding two separate substrates together preferably using a gold/gold thermocompression technique; one contains the cloverleaf resonator structures fabricated from SOI and bulk silicon substrates, and the other contains the support pillars, electrode metal, and through-wafer interconnects. A fourth wafer containing an array of etched cavities is solder-bonded to the device wafer in a vacuum, thus hermetically sealing each individual microgyroscope.

The resonator wafer A, preferably a SOI wafer, is preferably prepared first. On a bulk silicon base 1 having a preferable thickness of ≦500 μm, which is optionally lightly-doped bulk silicon about 1e15 cm⁻³, a silicon dioxide layer 2 having a preferable thickness of ≦2 μm is formed preferably by thermal oxidation at a temperature between 800° C. and 1000° C. On top of the silicon dioxide layer 2 a heavily doped silicon epi-layer, p-type, 1e19–1e20 cm⁻³ 3 is provided having a preferable thickness of 10 μm to 20 μm, as shown in FIGS. 1 a and 1 b.

Then the cloverleaf petal and spring of the resonator wafer A is prepared. Parts of the heavily doped silicon epi-layer 3 are preferably removed by photoresist lithography, deep reactive ion etching (DRIE) and photoresist removal, as shown in FIGS. 2 a and 2 b. Photoresist lithography and DRIE are described in inter alia Veljko Milanovic et al. “Deep Reactive Ion Etching for Lateral Field Emission Devices”, IEEE Electron Device Letters, Vol. 21, No. 6, June 2000, which is incorporated herein by reference.

The process preferably comprises:

-   -   1. The top silicon layer of the wafer is coated with a layer of         photoresist.     -   2. Light from an illuminator is projected through a mask that         contains the pattern to be created on the wafer. That light         patterns that pass through the mask are projected onto the         photoresist-coated layer.     -   3. The photoresist that is exposed to the light becomes soluble         and is rinsed away, leaving miniature images of the mask         pattern. It remains as an etch mask on the silicon surface of         the wafer.     -   4. Regions unprotected by photoresist are etched preferably by         gases utilizing Deep Reactive Ion Etching (DRIE). DRIE involves         repeated exposure of a photoresist-masked silicon wafer to an         etchant (usually SF₆) plasma in alternation with a passivant         (usually C₄F₈) plasma. So the etching process preferably cycles         between etching and deposition steps several times to achieve a         deep etching with a quite vertical profile. The etch rate,         profile and selectivity to the mask are controlled by adjusting         etch and passivation step efficiency or the time ratio of the         two steps. Average etch rate is around 2.7 μm/min, and etching         is terminated when the SiO₂ layer 2 is reached. The SiO₂ layer 2         serves as a stop layer.

5. After the DRIE process the photoresist is removed. Photoresist removal with solvents is a preferred process in the semiconductor manufacturing and is used extensively after any metal processing. Organic strippers may have any number of different components such as NMP, glycol ether, amine, and DMSO.

The process parameters for the photoresist lithography are preferably as follows:

-   -   a) Resist Application:         -   2.07 μm         -   AZI 1350J, 3500 RPM         -   100° C. Hotplate bake for 45 sec.     -   b) Resist Exposure:         -   Photomask # C1         -   Time=7 sec.         -   Mask Offset=0.2 μm     -   c) Develop & Bake:         -   MF351:H₂O, 1:5 for 60 sec         -   100C Hotplate Bake for 45 sec.

The bottom post wafer B is prepared next. On a bulk silicon base 1 having a preferable thickness of ≦500 μm, which is optionally lightly-doped bulk silicon layer (about 1e15 cm⁻³) 2 a silicon dioxide layer, having a preferable thickness of ≦2 μm, is formed preferably by thermal oxidation between 800° C. and 1000° C. as shown in FIGS. 3 a and 3 b.

Wafer B is bonded to resonator wafer A. The bondage between heavily-doped silicon epi-layer 3 of the bottom portion of wafer A and the silicon dioxide layer 2 of the wafer B may be achieved by heating at a temperature from 800° C. to 1000° C., as diagrammatically shown in FIGS. 4 a and 4 b. In this process the SiO₂ layer 2 of wafer B is preferably bonded to the heavily doped silicon epi-layer, 3 of the SOI wafer A. The epi-layer 3 is preferably p-type, 1e19–1e20 cm⁻³.

Then the bottom post B′ and rib pattern are prepared. The bulk silicon layer 1 and silicon dioxide layer 2 of the wafer B have been partially removed to yield a post B′ as shown in FIGS. 5 a and 5 b.

The process preferably comprises:

-   -   1. Coating the top silicon layer 1 of the wafer B with a layer         of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern to be created on the wafer B,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the silicon surface of the wafer B.     -   4. Etching silicon layer 1 unprotected by photoresist by gases         utilizing the deep reactive ion etch (DRIE).     -   5. Removing SiO₂ layer 2 of wafer B by CF₄/O₂ plasma etch, and     -   6. Removing photoresist on the surface of the post B′.

Then ohmic contacts are formed. On the heavily doped silicon epi-layer 3 several contacts 4 are preferably formed by sputtering metal. The contacts 4 are preferably placed symmetrically around the post B′. The contacts 4 contain preferably Ti/Pd/Au, Ti/Pt/Au or mixtures thereof. The contacts 4 are prepared for example by photoresist lithography, wet etching the metal and removing the photoresist (photoresist spray lithography, metallization Ti/Pt/Au and metal lift-off), as shown in FIGS. 6 a and 6 b. Metal liftoff is a common means of creating narrow metal lines for metals. A metal liftoff process is preferably done in a spray system. The process of resist photoresist, spray lithography, metallization and metal lift-off is described for example, in inter alia, Andrea Via et al. “Metal Lift-off on InP HBTs Using Carbon Dioxide Snow Spray” (see: www1.boc.com/eco-snow/pdf/CS-MAX%202002.pdf.)

The process preferably comprises:

-   -   1. Coating the heavily doped silicon epi-layer, p-type,         1e19–1e20 cm⁻³ 3 of the wafer A by metallization with sputter         metal (Ti/Pd/Au).     -   2. Coating metal (Ti/Pd/Au) on the layer 3 with a layer of         photoresist,     -   3. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the ohmic contacts 4         to be created, on the layer 3 of wafer A,     -   4. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the silicon surface of the wafer A,         Removing the metal which is not covered by photoresist by wet         etch,     -   5. Removing photoresist on the surface of the ohmic contacts 4.

The process for photoresist spray lithography, metallization Ti/Pt/Au and metal lift-off preferably comprises:

-   -   1. Coating layer 3 with a layer of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the ohmic contacts         Ti/Pt/Au 4 to be created, on the layer 3 of wafer A,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the silicon surface of the wafer A,         Removing the metal which is not covered by photoresist by wet         etch,     -   4. Depositing Ti/Pt/Au 4 by spray lithography,     -   5. Removing Ti/Pt/Au 4 covering the photoresist by a metal         lift-off process,     -   6. Stripping the remaining photoresist yielding a Ti/Pt/Au 4         pattern on the surface of wafer C.

Then a base wafer C is prepared. The preferred starting material 5 of the base wafer C has a preferable thickness of about ≦800 μm and preferably contains a moderately doped silicon substrate p-type, 1e 19 cm⁻³, as shown in FIGS. 7 a and 7 b.

On both surfaces of the preferred starting material 5 of the base wafer C a silicon dioxide layer 2 of ≦0.3 μm-thick is grown by thermal oxidation at a temperature preferably of about 950° C., as shown in FIGS. 8 a and 8 b.

Then a pillar fabrication is carried out. From the preferred starting material 5 a thickness of preferably about 5 μm to 8 μm is removed by photoresist lithography, wet etch SiO₂ and photoresist removal, wet KOH etch of silicon and SiO₂ removal in order to obtain pillars PI, as shown in FIGS. 9 a and 9 b.

The process preferably comprises:

-   -   1. Coating the top and bottom SiO₂ layer 2 of wafer C with a         layer of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the pillars PI to be         created, on the top layer 2 of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the SiO₂ layer 2 of the wafer C,     -   4. Removing the SiO₂ layer 2, which is not covered by         photoresist, by CF₄/O₂ plasma etch,     -   5. Removing 5–8 μm of moderate doped Si preferred starting         material 5 by wet KOH etch to produce a cavity CA,     -   6. Removing remaining photoresist, and     -   7. Removing SiO₂ layer 2 on the pillars and on the bottom layer         by CF₄/O₂ plasma etch.

On both surfaces of the preferred starting material 5 of the base wafer C (with pillars PI) a SiO₂ layer of ≦2 μm thick is provided, preferably by thermal oxidation at a temperature of about 1050° C., as shown in FIGS. 10 a and 10 b.

An ohmic contact metal Al 6 and interconnect metal Ti/Al 7 may be attached to the preferred starting silicon material 5 of the base wafer C by photoresist spray lithography and metal deposition and liftoff, as shown in FIGS. 11 a and 11 b.

The process preferably comprises:

-   -   1. Coating SiO₂ layer 2 with a layer of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the ohmic contact Al         6 to be created on the layer 2 of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the SiO₂ layer 2 of the wafer C,     -   4. Removing the SiO₂ layer 2 by wet etch which is not covered by         photoresist,     -   5. Depositing Al 6 by spray lithography,     -   6. Removing Al 6 covering the photoresist by a metal lift-off         process,     -   7. Stripping the remaining photoresist yielding an Al 6 pattern         on the surface of wafer C.

A layer of Ti/Pd/Au 8 was deposited preferably by Sputter Deposition of Ti/Pd/Au on the top surface, as shown in FIGS. 12 a and 12 b. Pd can be advantageously removed by wet etching.

The following process disclosed in FIGS. 13 to 17 is a preferred process to prepare a preparing a base wafer with through-wafer interconnects as a part of a vacuum packaged integrated microgyro with thru-wafer interconnects. A hole formation was performed to produce holes 7′, 7″, 7′″, in the bottom of wafer C, as shown in FIGS. 13 a and 13 b.

The process preferably comprises:

-   -   1. Coating the bottom SiO₂ layer 2 of wafer C with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the holes 7 to be         created, on the bottom layer 2 of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the SiO₂ layer 2 of the wafer C,     -   4. Removing the SiO₂ layer 2, which is not covered by         photoresist, by CF₄/O₂ plasma etch,     -   5. Removing moderate doped Si preferred starting material 5 by         Deep DRIE of Si to produce the holes 7,     -   6. Removing remaining photoresist

A Si₃N₄ layer 9 is preferably provided on the bottom of base wafer C preferably by PECVD of Si₃N₄ deposition, wherein a Si₃N₄ layer 9≦1.0 μm thick is preferably provided, as shown in FIGS. 14 a and 14 b.

A dielectric layer and Titanium metal etch at the bottom of wafer C is performed. The horizontal layer of Si₃N₄ 9 in the holes 7″ and 7′″ on the bottom of the base wafer C is removed, as shown in FIGS. 15 a and 15 b.

The process preferably comprises:

-   -   1. Coating the bottom Si₃N₄ 9 layer of wafer C with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the holes 7 to be         created, on the bottom layer 9 of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the Si₃N₄ 9 layer in the holes 7″ and         7′″ of the wafer C,     -   4. Removing the Si₃N₄ 9 layer in the holes 7″ and 7′″ which is         not covered by photoresist, by CF₄/O₂ plasma etch,     -   5. Ion Mill treatment of Ti metal layer to expose Pd metal of         Ti/Pd/Au 8 for electroplating and     -   6. Removing remaining photoresist.

A hole metal plating is carried out at the bottom of wafer C. The holes 7 on the bottom of the base wafer C are electroplated by copper electroplating, as shown in FIGS. 16 a and 16 b.

The process preferably comprises:

-   -   1. Coating the bottom Si₃N₄ 9 layer of wafer C with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for the holes 7 to be         created, on the bottom layer 9 of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the Si₃N₄ 9 layer in the holes 7 of the         wafer C,     -   4. Electroplating with copper 14 in the holes 7, and     -   5. Removing remaining photoresist.

Si₃N₄ 9 layer on the bottom of the wafer C was then removed preferably by CF₄/O₂ as shown in FIGS. 17 a and 17 b.

Seal ring metal Ti/Pd/Au 8 a, drive/sense electrodes Ti/Pd/Au 8 b and wafer bonding metal Ti/Pt/Au 8 c may be provided by photoresist lithography and metal deposition and liftoff, as shown in FIGS. 18 a and 18 b.

The process preferably comprises:

-   -   1. Coating the top surface layer Ti/Pd/Au 8 layer of wafer C         with a layer of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places were Ti/Pd/Au 8 layer         shall be removed on the top of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the Ti/Pd/Au 8 layer on the wafer C,     -   4. Wet etching of Ti/Pd/Au 8 and creating seal ring metal         Ti/Pd/Au 8 a, drive/sense electrodes Ti/Pd/Au 8 b and wafer         bonding metal Ti/Pt/Au 8 c, and     -   5. Removing remaining photoresist.

As a next step a post hole etch 5′ is preferably carried out by photoresist lithography (spray on thick resist), CF₄/O₂ plasma etch of silicon dioxide in the hole region, DRIE of silicon hole and photoresist removal as shown in FIGS. 19 a and 19 b.

The process preferably comprises:

-   -   1. Coating the top surface of wafer C with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the place for the hole region on         the top surface of wafer C,     -   3. Washing the exposed regions of the photoresist layer and         leaving a mask on the top surface of the wafer C,     -   4. CF₄/O₂ plasma etch of silicon dioxide in the hole region,     -   5. DRIE remove to create a silicon hole 5′, and     -   6. Stripping the remaining photoresist layer.

As a next step a bonding of resonator wafer A according to FIG. 6 b and to base wafer C according to FIG. 19 b is carried out preferably by an Au to Au thermocompression bond at a temperature of 300° C. to 400° C., as shown in FIGS. 20 a and 20 b. The bonding is carried out between the contacts 4 of resonator wafer A-B and the seal ring metal 8 a of the base wafer C. Post B′ of resonator wafer A-B fits into the post hole 5′ of base wafer C.

The post fabrication on wafer A is preferably carried out by photoresist lithography (spray on thick resist), CF₄/O₂ plasma etching of silicon dioxide, photoresist removal by dry etch. Thereby a post A′ and optional frame formation in the top layer A″ is obtained, as shown in FIGS. 21 a and 21 b.

The process preferably comprises:

-   -   1. Coating the top surface of wafer A with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the place for the hole region on         the top surface of wafer A,     -   3. Washing the exposed regions of the photoresist layer and         leaving a mask on the top surface of the wafer A,     -   4. DRIE remove of silicon from wafer A,     -   5. CF₄/O₂ plasma etch of silicon dioxide from wafer A, whereby a         post A′ and optional frame formation in the top layer A″ is         obtained, and     -   6. Stripping the remaining photoresist layer.

A cap wafer D is prepared with a preferred starting material of lightly doped bulk silicon 1 having a thickness of ≦800 μm and having on top and bottom a thin silicon dioxide layer 2, as shown in FIGS. 22 a and 22 b.

A backside metallization is carried out by photoresist lithography and metal deposition and liftoff. Thereby Ti/Pt/Au 8 and solder metal 12 are attached, as shown in FIGS. 23 a and 23 b.

The process preferably comprises:

-   -   1. Coating the bottom surface of cap wafer D with a layer of         photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern, namely the places for seal ring Ti/Pt/Au 8         and solder metal 12 to be attached, on the bottom surface of         wafer cap wafer D,     -   3. Washing the exposed regions of the photoresist layer and         leaving a mask on the top surface of the wafer D,     -   4. Depositing Ti/Pt/Au on the bottom surface of cap wafer D,     -   5. Depositing solder metal 12 on the bottom surface of cap wafer         D,     -   6. Removing excess Ti/Pt/Au 8 and solder metal 12 covering the         photoresist by a metal lift-off process,     -   7. Stripping remaining photoresist yielding a seal ring Ti/Pt/Au         8 and solder metal 12.

Then backside cavity 13 a is preferably formed on the cap wafer D by spraying thick photoresist on the backside, DRIE etch of SiO₂, DRIE cavities and remove photoresist, as shown in FIGS. 24 a and 24 b.

The process preferably comprises:

-   -   1. Coating the bottom silicon dioxide layer 2 of the cap wafer D         with a layer of photoresist,     -   2. Projecting light from an illuminator through a mask that         contains the pattern to be created on bottom layer 2 of the cap         wafer D,     -   3. Washing the exposed regions of the photoresist layer and         leaving an etch mask on the bottom silicon dioxide layer 2 of         the cap wafer E,     -   4. Removing SiO₂ layer 2 of wafer B by CF₄/O₂ plasma etch,     -   5. Etching silicon layer 1 unprotected with photoresist by gases         utilizing the deep reactive ion etch (DRIE) on the bottom of the         cap wafer D, and     -   6. Removing photoresist from the bottom silicon dioxide layer 2         of the cap wafer D yielding two cavities 13.

The cap wafer D is preferably bonded to the base wafer C. The cap wafer D is positioned on top of base wafer C. A solder bond is carried out at low temperature at about 200° C. between the solder metal 12 of the cap wafer D and the seal ring metal 8 a of the base wafer C, as shown in FIGS. 25 a and 25 b.

The present invention can be used for cell phone applications where the gyros are mounted directly on a PC board. In addition, for high g applications, the changes in the stray capacitance that can occur if the wire bonded interconnects move can create false signals and noise. Finally, if vertical stacking of the Si microgyro with its ASIC is desirable for 3-D (but separate wafer) integration, ball-grid array interconnect techniques are necessary.

This invention is extremely important in the overall packaging concepts for I*Star inertial instruments. Different customers require different package and interconnect designs for use in their products. Automotive users still prefer to use wire bonding and plastic hybrid packages for many of their applications. However, other users such as wireless manufacturers or military users such as Raytheon will require even lower cost and more rugged packaging concepts. In general, the IC industry is moving toward ball-grid array technology for advanced packaging designs.

Finally, the manufacturing yield and vacuum lifetime may be improved with the present design since the solder on the capping wafer seal ring makes a vacuum seal to a completely planar metal seal ring on the base wafer. The previous design could produce undulations in the bottom seal ring due to the Ti/Al interconnects.

Although certain preferred embodiments of the present invention have been described above, these should not be construed as limiting the scope of the invention but as merely providing illustrations of some of the presently preferred embodiments of this invention. Those skilled in the art will appreciate the fact that both the order in which the described processes are carried out and the described process parameters may be varied if needed to suit local requirements. 

1. A method of manufacturing a cloverleaf microgyroscope containing an integrated post comprising: a) attaching a post wafer to a resonator wafer, b) forming a bottom post from the post wafer, c) preparing a base wafer with through-wafer interconnects, d) attaching the resonator wafer to the base wafer, wherein the bottom post fits into a post hole in the base wafer, e) forming a top post from the resonator wafer, wherein the bottom and top post are formed symmetrically around the same axis, and f) attaching a cap wafer on top of the base wafer.
 2. The method according to claim 1, wherein the through-wafer interconnects comprise copper, copper alloys and mixtures thereof.
 3. The method according to claim 1, wherein the top post is formed of a bulk silicon base having a thickness of ≦500 μm, a silicon dioxide layer of ≦2 μm and a heavily-doped Silicon epi-layer of 10 μm–20 μm, p-type, 1e19–1e20 cm⁻³.
 4. The method according to claim 1, wherein the bottom post is formed of a bulk silicon base having a thickness of ≦500 μm and a silicon dioxide layer of ≦2 μm.
 5. The method according to claim 1, wherein the base wafer is manufactured of substrate containing moderately doped silicon substrate p-type, 1e19 cm⁻³ with a thickness of about ≦800 μm.
 6. The method according to claim 1, wherein ohmic contacts and interconnect metals containing Al or Al/Ti are formed preferably on the base wafer before the resonator wafer is attached to the base wafer.
 7. The method according to claim 1, wherein electrodes, bond pad, and wire bond metal are formed on the base wafer before the resonator wafer is attached to the base wafer.
 8. The method according to claim 1, wherein electrodes, bond pad, and wire bond metal are formed on the base wafer before the resonator wafer is attached to the base wafer.
 9. The method according to claim 1, wherein a seal ring containing Ti/Pt/Au is formed on the base wafer before the resonator wafer is attached to the base wafer.
 10. The method according to claim 1, wherein the cap wafer is manufactured of lightly doped bulk silicon having a thickness of ≦800 μm.
 11. The method according to claim 1, wherein an opening is prepared in the cap wafer, a wire is led through the opening in the cap wafer and bonded to a bonding pad on the base wafer.
 12. The method according to claim 1, wherein parts of heavily doped silicon layer of the resonator wafer are removed by resist lithography and photoresist removal.
 13. The method according to claim 1, wherein the bondage between heavily-doped silicon epi-layer of the resonator and silicon dioxide layer of the post wafer is achieved by heating at a temperature from 800° C. to 1000° C.
 14. The method according to claim 1, wherein bulk silicon layer and silicon dioxide of the post wafer are partially removed to yield the bottom post by resist lithography, CF₄/O₂ plasma etch SiO₂ and removal of photoresist.
 15. The method according to claim 1, wherein the bonding of the resonator wafer to the base wafer is carried out by an Au to Au thermo-compression bonding at a temperature from 200° C. to 500° C.
 16. The method according to claim 1, wherein a bulk silicon layer and silicon dioxide of the resonator wafer are partially removed to yield a top post by resist lithography, CF₄/O₂ plasma etch of SiO₂ and removal of photoresist.
 17. The method according to claim 1, wherein the bondage between the cap wafer and the base wafer is carried out with solder metal at a temperature at about 100° C. to 300° C.
 18. The method according to claim 1, wherein a hole in the cap wafer is formed by wet etch of silicon and vacuum oven baking.
 19. The method according to claim 1, wherein the wire bonding is carried out by saw cutting of cap wafer and ball bonding of wires to wire bonding pad of the base wafer. 